ULDPE SL 4100G
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 0.912 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 1.0 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D2457 | 75 | |
| Haze ratio | ISO 14782 | 8.0 % |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | ISO 7765-1/B | 850 g | |
| elongation | ISO 527-3 | 760 % | |
| Elmendorf tear strength | ASTM D1922 | 690 g | |
| ASTM D1922 | 850 g | ||
| film thickness | 40 µm | ||
| Tensile modulus | ISO 527-3 | 120 MPa | |
| ISO 527-3 | 135 MPa | ||
| tensile strength | ISO 527-3 | 6.50 MPa | |
| ISO 527-3 | 6.20 MPa | ||
| ISO 527-3 | 31.0 MPa | ||
| ISO 527-3 | 30.0 MPa | ||
| elongation | ISO 527-3 | 640 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM D1525 | 92.0 °C | |
| melting temperature | DSC | 122 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.