Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.18 g/cm³ |
| Shrinkage rate | | ASTMD955 | 0.60到1.0 % |
| Shrinkage rate | | ASTMD955 | 0.60到1.0 % |
| density | | ASTMD792 | 1.18 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 100 |
| Rockwell hardness | R-Scale | ASTMD785 | 100 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 130 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 130 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTMD638 | 3.0 % |
| Flexural modulus | | ASTMD790 | 5880 MPa |
| bending strength | | ASTMD790 | 137 MPa |
| tensile strength | | ASTMD638 | 88.3 MPa |
| tensile strength | | ASTMD638 | 88.3 MPa |
| elongation | | ASTMD638 | 3.0 % |
| Flexural modulus | | ASTMD790 | 5880 MPa |
| bending strength | | ASTMD790 | 137 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 147 °C |
| Heat distortion temperature | | ASTMD648 | 95.0 °C |
| Heat distortion temperature | Melting Temperature | ASTMD648 | 163 °C |
| Heat distortion temperature | | ASTMD648 | 147 °C |
| Heat distortion temperature | Melting Temperature | ASTMD648 | 163 °C |
| Heat distortion temperature | | ASTMD648 | 95.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.