Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.21 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| FlameRating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO1172 | 15 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 15 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 80 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 5500 MPa |
| Tensile stress | Break | ISO527-2/5 | 120 MPa |
| Tensile strain | Break | ISO527-2/5 | 5.5 % |
| Flexural modulus | | ISO178 | 4000 MPa |
| Bending stress | | ISO178 | 160 MPa |
| Fracture bending strain | | ISO178 | 8.5 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | DINEN11357-1 | 222 °C |
| | ISO75-2/B | 216 °C |
| | ISO75-2/A | 195 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.