ABS FR3002
0
- Usages:Thin walled components
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO294-4 | 0.60 % | |
| ISO294-4 | 0.60 % | ||
| Water absorption rate | ISO62 | 0.50 % | |
| ISO62 | 0.20 % | ||
| ISO1133 | 19 cm³/10min | ||
| density | ISO1183 | 1.18 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO180/1A | 30 kJ/m² | |
| tensile strength | ISO527-2 | 60 MPa | |
| elongation at break | ISO527-2 | >50 % | |
| Tensile modulus | ISO527-2 | 2700 MPa |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| fire rating | UL-94 | 0.75mm | |
| UL-94 | 0.90mm V-0 | ||
| UL-94 | 1.00mm V-0 | ||
| UL-94 | 1.50mm V-0 | ||
| UL-94 | 1.80mm V-0,5VB |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| IEC60093 | 1E+16 Ω.cm | ||
| Surface Resistivity | IEC60093 | 1E+16 Ω.cm | |
| Dielectric Strength | IEC60243-1 | 35 KV/mm | |
| dielectric constant | IEC60250 | 3.10 1MHz | |
| Dissipation Factor | IEC60250 | 6E-03 1MHz | |
| IEC60112 | 300 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/Bf | 92 °C | ||
| ISO75-2/Af | 84 °C | ||
| vicat | ISO306/B50 | 97 °C | |
| ISO11359-2 | 7.6E-05 cm/cm／°C | ||
| ISO11359-2 | 8E-05 cm/cm／°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.