Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| shelf-life | | | 52 wk |
| Post curing time | | | 2.0 hr |
| Post curing time | | | 0.50 hr |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | | 0.90 % |
| pH value | | | 8.0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Carrier | | | Glassfabric |
| Ionic Chloride | | | 110 ppm |
| IonicPotassium | | | 9 ppm |
| IonicSodium | | | 35 ppm |
| LapShear | | | 22.8 MPa |
| LapShear | | | 25.5 MPa |
| LapShear | | | 110 µS/cm |
| LapShear | | | 0.34 % |
| LapShear | | | 6.0 month |
| LapShear | | | 0.16 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | | 6140 MPa |
| Tensile modulus | | | 4350 MPa |
| Tensile modulus | | | 2000 MPa |
| Tensile modulus | | | 1860 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | | 9.1E+12 ohms·cm |
| dielectric strength | | | 820 kV/mm |
| dielectric constant | | | 5.70 |
| Dissipation Factor | | | 0.012 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | 55.0 °C |
| | | 8.5E-05 cm/cm/°C |
| | | 3E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 0.90 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.