Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D1505 | 0.949 g/cm³ |
| Carbon black content | | ASTM D1603 | 2.5 % |
| Environmental stress cracking resistance | | ASTM D1693 | >5000 hr |
| melt mass-flow rate | | ASTM D1238 | 0.23 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 59 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Light absorption coefficient | | ASTM D3349 | >400 Abs/mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTM D638 | 800 % |
| tensile strength | | ASTM D638 | 29.4 MPa |
| aging | Test Condition | Test Method | Test Result |
|---|
| Elongation retention rate | | ASTM D638 | >85 % |
| Change rate of tensile strength in air | | ASTM D638 | >85 % |
| Oven aging | | | 10.0 day |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTM D150 | 5E-04 |
| dielectric constant | | ASTM D150 | 2.40 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | -76.0 °C |
| Oxidation induction time (OIT) | | ASTM D3895 | >100 min |
| Environmental Stress Cracking Resistance (ESCR) | | ASTM D2951 | >96 hr |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.