Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 0.493to2.00 |
| saturation | | % | 0.20to0.87 |
| Apparent density | | g/cm³ | 1.04to1.61 |
| Shrinkage rate | | mm/mm | 0.003-193.0E-3 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 79to88 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | % | 86.8to99.0 |
| refractive index | | | 1.508to1.546 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | % | 30to34 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Compression Modulus | | | 21.59to2800.0 Mpa |
| fracture | | | 13.45to246.9 Mpa |
| limiting pv value | | | 45.72to53.03 Mpa |
| yield | | | 30.0to75.86 Mpa |
| yield | | | 26.34to252.41 Mpa |
| yield | | | 10.9to180.0 Mpa |
| yield | | % | 0.40to6.7 |
| Flexural modulus | | | 1.17to12689.66 Mpa |
| fracture | | % | 0.63to23 |
| fracture | | | 57.17to62.34 Mpa |
| compressive strength | | | 16.76to201.38 Mpa |
| Tensile modulus | | | 186.21to18413.79 Mpa |
| shear strength | | | 3.9to53.45 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 0.004to0.022 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | sec | 177to180 |
| dielectric strength | | | 3.34to5.23 |
| Volume resistivity | | | 3.16to5.29 |
| Surface Resistivity | | ohms | 4.0E+10到1.5E+16 |
| Dissipation Factor | | | 6.0E-4到0.040 |
| Test Condition | Test Method | Test Result |
|---|
| Curing Time | | hr | 2.5to25 |
| stripping time | | min | 0.54to270 |
| melt viscosity | | Pa·s | 0.550to126 |
| STORAGE STABILITY | | min | 28to160 |
| tensile strength | | | 17.17to56.55 Mpa |
| density | | g/cm³ | 0.913to1.63 |
| shelf-life | | wk | 24to54 |
| Thermosetting mixed viscosity | | cP | 14.0to23500 |
| Color | | | AmberBlackClear/TransparentColorlessGrey |
| STORAGE STABILITY | | min | 1.0to3300 |
| Viscosity | | Pa·s | 0.055to11 |
| Post curing time | | hr | 0.50to7.7 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | °C | 68to157 |
| Linear coefficient of thermal expansion | | mm/mm/°C | 81.3E-5到127.0E-5 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.