Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ISO60 | 0.60 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.61 % |
| Shrinkage rate | | ISO2577 | 0.15 % |
| Shrinkage rate | | ISO2577 | 0.59 % |
| Shrinkage rate | | ISO2577 | 0.14 % |
| Water absorption rate | | ISO62 | 7.0 % |
| Water absorption rate | | ISO62 | 2.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 110 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 650 °C |
| Extreme Oxygen Index 7 | | ISO4589-2 | 22 % |
| BurningBehavior8 | | ISO3795 | passed |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISO Shortcut | | ISO1874 | PA6/66HI,GR,14-040,GF15 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 4500 Mpa |
| Tensile stress | | ISO527-2/5 | 85.0 Mpa |
| Tensile strain | | ISO527-2/5 | 4.5 % |
| Flexural modulus | | ISO178/A | 4000 Mpa |
| Bending stress | | ISO178/A | 125 Mpa |
| Bending stress | | ISO178/A | 130 Mpa |
| | ISO178/A | 5.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 80 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 70 kJ/m² |
| Multi axis Instrumented Impact Energy | | ISO6603-2 | 4.80 J |
| Multi axis Instrumented Impact Energy | | ISO6603-2 | 13.0 J |
| Multi axis Instrumented Peak Impact Force | | ISO6603-2 | 650 N |
| Multi axis Instrumented Peak Impact Force | | ISO6603-2 | 1000 N |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| Volume resistivity | | IEC60093 | 1E+13 ohms·cm |
| dielectric strength | | IEC60243-1 | 43 KV/mm |
| | IEC60250 | 3.50 |
| | IEC60250 | 3.20 |
| Dissipation Factor | | IEC60250 | 6E-03 |
| Dissipation Factor | | IEC60250 | 0.015 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/C | 60.0 °C |
| vicat | | ISO306/B50 | 200 °C |
| vicat | | ISO306/B120 | 200 °C |
| Melting temperature 5 | | ISO11357-3 | 214 °C |
| | ISO11359-2 | 4E-05 cm/cm/°C |
| | ISO11359-2 | 1.5E-04 cm/cm/°C |
| | ISO75-2/B | 205 °C |
| | ISO75-2/A | 175 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.