Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | mm/mm | 0.019到137.2E-3 |
| density | | | 1.70到2.03 |
| Apparent density | | g/cm³ | 0.68到0.95 |
| Water absorption rate | | % | 0.10到0.16 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Barcol Hardness | | | 9.1到50 |
| Rockwell hardness | | | 51到110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | % | 24到47 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | % | 0.60到1.1 |
| compressive strength | | Mpa | 136.55到180.0 |
| yield | | Mpa | 41.24到55.72 |
| yield | | Mpa | 68.97到113.79 |
| Flexural modulus | | Mpa | 9310.34到18344.83 |
| Tensile modulus | | Mpa | 9586.21到20137.93 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 0.007到0.061 |
| Charpy Notched Impact Strength | | J/m | 0.008到0.010 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | sec | 180到191 |
| dielectric strength | | V/mil | 260到380 |
| dielectric constant | | | 4.20到6.15 |
| Dissipation Factor | | | 6.3E-3到0.028 |
| Compared to the Leakage Tracking Index (CTI) | | V | 500到600 |
| Volume resistivity | | ohms·cm | 2.5E+14到6.6E+15 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 258到260 |
| | mm/mm/°C | 61.0E-5到101.6E-5 |
| Continuous use temperature | | °C | 165到222 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.