Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 0.20 -- |
| density | | g/cm³ | 1.56 -- |
| Shrinkage rate | | % | 0.80 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | | 81 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| Hot filament ignition temperature | | °C | 650 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 16000 12700 |
| Tensile stress | | MPa | 210 150 |
| Tensile strain | Break | % | 2.0 2.5 |
| Flexural modulus | | MPa | 14000 12500 |
| Bending stress | | MPa | 290 270 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 8.5 -- |
| Charpy Notched Impact Strength | | kJ/m² | 13 16 |
| Charpy Notched Impact Strength | | | 无断裂 -- |
| Charpy Notched Impact Strength | | kJ/m² | 12 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 220 -- |
| | °C | 215 -- |
| vicat | | °C | >200 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.