Unspecified FORMULA P COMP 5410 M1
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 1.0到1.2 % | |
| density | ISO1183/A | 0.950 g/cm³ | |
| melt mass-flow rate | ISO1133 | 15 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | Yield | ISO527-2 | 26.0 MPa |
| Break | ISO527-2 | 23.0 MPa | |
| Tensile strain | Break | ISO527-2 | 50 % |
| Flexural modulus | ISO178 | 2000 MPa | |
| Scratch Resistance | 内部方法 | <1.00 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO180 | 10 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO306/B | 72.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.