POM Celcon® M90CF2001 CELANESE NANJING
54
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.41 g/cm³ | |
| ISO 1183 | 1.41 g/cm³ | ||
| melt mass-flow rate | ASTM D1238 | 9.0 g/10min | |
| Melt volume flow rate | ISO 1133 | 8.00 cm3/10min | |
| Shrinkage rate | ASTM D955 | 2.2 % | |
| ASTM D955 | 1.8 % | ||
| ISO 294-4 | 1.9 % | ||
| ISO 294-4 | 2.0 % | ||
| Water absorption rate | ISO 62 | 0.75 % | |
| ISO 62 | 0.20 % | ||
| DensityMelt | 内部方法 | 1.200 g/cm³ | |
| SpecificHeatCapacity of Melt | 内部方法 | 2210 J/kg/°C | |
| ThermalConductivityofMelt | 内部方法 | 0.16 W/m/K |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 6.0 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 180 kJ/m² | |
| ISO 179/1eU | 190 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 5.7 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179/1eA | 6.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 2760 Mpa | |
| tensile strength | ASTM D638 | 94.5 Mpa | |
| ASTM D638 | 60.7 Mpa | ||
| ASTM D638 | 34.5 Mpa | ||
| ISO 527-2/1A/50 | 65.0 Mpa | ||
| Tensile strain | ISO 527-2/1A/50 | 10 % | |
| Tensile creep modulus | ISO 899-1 | 2450 Mpa | |
| ISO 899-1 | 1350 Mpa | ||
| Flexural modulus | ISO 178 | 2550 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 3E+16 ohms | |
| Volume resistivity | ASTM D257 | 1E+14 ohms·cm | |
| IEC 60093 | 8E+14 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| Effective thermal diffusivity coefficient | 内部方法 | 0.0485 cSt | |
| Heat distortion temperature | ISO 75-2/B | 158 °C | |
| ASTM D648 | 110 °C | ||
| ISO 75-2/A | 101 °C | ||
| melting temperature | ASTM D3418 | 165 °C | |
| ISO 11357-3 | 165 °C | ||
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.2E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.