PA9T G1300H

Form：Powder | Color：true qualities | Filler：glass fibre 30 %

Properties:

High temperature resistanHigh mobilityHigh rigiditywear resistantHigh impact resistanceGlass fiber reinforced

Typical Applications:

Computer caseFitness equipmentLaptop caseEngine partsBottle capCasters

Supplier(0)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Computer case \| Fitness equipment \| Laptop case \| Engine parts \| Bottle cap \| Casters
Properties:	High temperature resistan \| High mobility \| High rigidity \| wear resistant \| High impact resistance \| Glass fiber reinforced
Color:	true qualities
Form:	Pellets
Filler:	glass fibre 30%

Certificates

TDS

Technical Data Sheet

Other	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.41	g/cm³
Fiberglass content			30	%
Molding shrinkage rate		ISO 2577	0.2-0.4	%
Molding shrinkage rate	Molding shrinkage rate		ISO 2577	0.8-1.0	%
水吸收率	平衡	ISO 62	0.3	%
Mechanical Properties	Test Condition	Test Method	Test Result	Test Unit
Gap cantilever beam impact test	23℃	ISO 180-1A	10.0	KJ/m²
Flexural strength	10mm/min	ISO 178	260	MPa
Flexural elasticity	2mm/min	ISO 178	9200	MPa
Tensile yield strength	10mm/min	ISO 527-2	180	MPa
Thermal Properties	Test Condition	Test Method	Test Result	Test Unit
Thermal distortion temperature	0.45MPa	ISO 75-2	285	℃
Thermal distortion temperature	Thermal distortion temperature	1.80MPa	ISO 75-2	265	℃
Melt index	330℃/2.16KG		70.3	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
volume resistivity		IEC60093	1015	Q·cm
dielectric strength		IEC60243-1	21	kV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.