Other performance	Test Condition	Test Method	Test Result	Test Unit
gloss	60°		93
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break	50mm/min	ISO 527	20	%
bending strength	2mm/min 80×10×4	ISO 178	68	Mpa
Tensile stress	50mm/min，Yield	ISO 527	43	Mpa
tensile strength	50mm/min	ISO 527	33	Mpa
Tensile modulus	1mm/min	ISO 527	2400	Mpa
Bending modulus	2mm/min 80×10×4	ISO 178	2300	Mpa
Rockwell hardness	t=6.4mm	ISO 2039-2	111	R标尺
melt mass-flow rate	220℃；10kg	ISO 1133	37	g/10min
Impact strength of cantilever beam gap	23℃	ISO 180/1A	17	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	HB	类别
Vicat softening temperature	50N:120K/h	ISO 306	94	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.05	g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.