Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.56 g/cm³ |
| Shrinkage rate | | | 0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Hot filament ignition temperature | | IEC60695-2-13 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO527-2 | 3.0 % |
| Flexural modulus | | ISO178 | 12000 MPa |
| Bending stress | | ISO178 | 290 MPa |
| Tensile stress | Yield | ISO527-2 | 225 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180 | 16 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| dielectric strength | | IEC60243-1 | 22 kV/mm |
| CTI | | IEC60112 | 550 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO3146 | 222 °C |
| Heat distortion temperature | | ISO75-2/B | 220 °C |
| Heat distortion temperature | | ISO75-2/A | 215 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare