Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183/A | 1.22 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO7619 | 52 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 160 MPa |
| Wear amount | | ISO4649-A | 30.0 mm³ |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 25 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | NoBreak |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | DIN53504 | 11.0 MPa |
| Tensile stress | | DIN53504 | 14.0 MPa |
| Tensile stress | | DIN53504 | 26.0 MPa |
| Tensile stress | Yield | DIN53504 | 40.0 MPa |
| Tensile stress | Yield | DIN53504 | 50.0 MPa |
| elongation | | DIN53504 | 550 % |
| elongation | Break | DIN53504 | 550 % |
| tear strength | | ISO34-1 | 130 kN/m |
| compression set | | ISO815 | 30 % |
| compression set | | ISO815 | 50 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.