Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.70to1.85 g/cm³ |
| Shrinkage rate | | | 0.15to0.35 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Compression Molded | ASTM D638 | 36.5 MPa |
| Flexural modulus | Compression Molded | ASTM D790 | 10300 MPa |
| bending strength | Compression Molded | ASTM D790 | 103 MPa |
| Poisson's ratio | | | 0.30 |
| Tensile modulus | Compression Molded | ASTM D638 | 12400 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | Compression Molded | ASTM D256 | 370 J/m |
| Suspended wall beam without notch impact strength | Compression Molded | ASTM D256 | 510 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 15 kV/mm |
| arc resistance | | ASTM D495 | >180 sec |
| Compared to the Leakage Tracking Index (CTI) | | ASTM D2303 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | | 0.30 W/m/K |
| RTI Elec | | UL 746 | 130 °C |
| RTI Imp | | UL 746 | 130 °C |
| RTI Str | | UL 746 | 130 °C |
| Linear coefficient of thermal expansion | | | 2.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 3.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.