Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| STORAGE STABILITY | | | 1400 min |
| stripping time | | | 20 min |
| stripping time | | | 10 min |
| Post curing time | | | 16到24 hr |
| Post curing time | | | 16到24 hr |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.14 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore A | ASTMD2240 | 92到94 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| AbrasionIndex | | | 498 |
| AbrasionIndex | | | 758 |
| AbrasionIndex | | | 2000 % |
| AbrasionIndex | | | 2200 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Wear and tear volume - Reflective volloss | | | 29.0 mm³ |
| Wear and tear volume - Reflective volloss | | | 19.0 mm³ |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD412 | 36.0 MPa |
| tensile strength | | ASTMD412 | 43.4 MPa |
| elongation | | ASTMD412 | 520 % |
| elongation | | ASTMD412 | 600 % |
| tear strength | | ASTMD624 | 75.0 kN/m |
| tear strength | | ASTMD624 | 92.8 kN/m |
| tear strength | | ASTMD470 | 25 kN/m |
| tear strength | | ASTMD470 | 28 kN/m |
| ReboundResilience - DropBall | | | 64 % |
| Tensile stress | | ASTMD412 | 8.00 MPa |
| Tensile stress | | ASTMD412 | 9.65 MPa |
| compression set | | ASTMD395B | 27 % |
| compression set | | ASTMD395B | 25 % |
| compression set | | ASTMD395B | 45 % |
| compression set | | ASTMD395B | 42 % |
| Basho elasticity | | ASTMD2632 | 52 % |
| Tensile stress | | ASTMD412 | 11.4 MPa |
| Tensile stress | | ASTMD412 | 12.8 MPa |
| Basho elasticity | | ASTMD2632 | 52 % |
| ReboundResilience - DropBall | | | 64 % |
| film | Test Condition | Test Method | Test Result |
|---|
| Tear resistance of pants | | ASTMD1938 | 44.8 N/mm |
| Tear resistance of pants | | ASTMD1938 | 81.4 N/mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.