POM 527UV DUPONT USA

Form：Granules | Grade：Weather resistant grade

Properties:

PhotostabilityLow wearWeather resistance

Typical Applications:

Automotive Interior PartsAutomotive sectorAutomotive interior parts

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Automotive Interior Parts \| Automotive sector \| Automotive interior parts
Properties:	Photostability \| Low wear \| Weather resistance

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	8.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	9.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	260	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	260	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	8.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	21	mm/min
UL flame retardant rating	0.8mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	0.8mm	IEC 60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B
Atomization	F-value(refraction)4	ISO 6452	90	%
Atomization	Atomization	G-value(condensate)	ISO 6452	2E-04	g
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Yield	ISO 527-2	17	%
Nominal tensile fracture strain		ISO 527-2	30	%
Bending modulus		ISO 178	3000	Mpa
bending strength		ISO 178	77.0	Mpa
Poisson's ratio		ISO 527	0.37
tensile strength	Yield	ISO 527-2	70.0	Mpa
Tensile modulus		ISO 527-2	3100	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 11357-3	178	°C
Vicat softening temperature	--	ISO 306/B50	160	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	174	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	95.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	163	°C
AnnealingTime-Optional			30.0	min/mm
AnnealingTemperature			160	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.2E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.42	g/cm³
melt mass-flow rate	190°C/2.16kg	ISO 1133	15	g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	13.0	cm3/10min
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20	%
	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	1.2	%
	Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	0.50	%
Shrinkage rate	MD	ISO 294-4	2.0	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	1.9	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 0
Dissipation factor	1MHz	IEC 60250	5.6E-03
Dissipation factor	Dissipation factor	100Hz	IEC 60250	2.1E-03
Relative permittivity	1MHz	IEC 60250	3.80
Relative permittivity	Relative permittivity	100Hz	IEC 60250	3.80
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Surface resistivity		IEC 60093	2E+13	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale	ISO 2039-2	120
Rockwell hardness	Rockwell hardness	M-Sale	ISO 2039-2	92
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Odor		VDA270	6.00
Emission		VDA275	<8.00	mg/kg
EmissionofOrganicCompounds		VDA277	16.0	µgC/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.