ABS P2HGV BK901510 INEOS USA

Form：Granules | Grade：Injection grade

Properties:

heat-resistinghigh strengthHigh rigidityFiller: Glass fiber reinfFiller by weight

Typical Applications:

Automotive sectorApplication in the automotive field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector \| Application in the automotive field
Properties:	heat-resisting \| high strength \| High rigidity \| Filler: Glass fiber reinf \| Filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	18	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179	20	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Break,23°C	ISO 527-2	74.0	Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2	74.0	Mpa
Tensile modulus		ISO 527-2	5500	Mpa
bending strength		ISO 178	101	Mpa
Bending modulus		ISO 178	5400	Mpa
Tensile strain	Break,23°C	ISO 527-2	2.0	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ISO 11359-1	4E-05	cm/cm/°C
Vicat softening temperature		ISO 306/B50	105	°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	102	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	106	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
ash content			16	%
Shrinkage rate		ISO 294-4	0.20-0.40	%
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	3.00	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	IEC 60250	6E-03
Dissipation factor	Dissipation factor	100Hz	IEC 60250	5E-03
Relative permittivity	1MHz	IEC 60250	3.10
Relative permittivity	Relative permittivity	100Hz	IEC 60250	2.90
Dielectric strength	1.50mm	IEC 60243-1	32	KV/mm
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Surface resistivity		IEC 60093	1E+14	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	135	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.