Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 23 g/10min |
| Shrinkage rate | | 内部方法 | 0.40-0.60 % |
| density | | ASTM D792 | 1.08 g/cm³ |
| density | | ISO 1183 | 1.08 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 102 |
| Rockwell hardness | | ISO 2039-2 | 102 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ISO 14782 | 3.0 % |
| transmissivity | | ISO 13468 | 85.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 40.0 Mpa |
| tensile strength | | ISO 527-2 | 45.0 Mpa |
| elongation | | ASTM D638 | 40 % |
| Tensile strain | | ISO 527-2 | 16 % |
| Flexural modulus | | ASTM D790 | 1810 Mpa |
| Flexural modulus | | ISO 178 | 1830 Mpa |
| bending strength | | ASTM D790 | 61.0 Mpa |
| bending strength | | ISO 178 | 64.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 13 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 190 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 150 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 80.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 74.0 °C |
| vicat | | | 85.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.