ABS TAIRILAC® AG15A0 FCFC TAIWAN
1849
- Properties:High rigidityCharacteristic: High rigiGeneral molding
- Usages:FootwearToyShellElectrical appliancesPlastic boxheelToyClock housing
- Certificates:FDAULMSDS
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 200℃×5kgf(49N) | ASTM D-1238(ISO 1133) | 1.7 | g/10min |
| 220℃×10kgf(98N) | ASTM D-1238(ISO 1133) | 19 | g/10min | |
| Combustibility | FILE NO. E162823 | UL-94 | 1/16"HB All Color | |
| density | ASTM D-792(ISO 1183) | 1.05 | 23℃/23℃ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| bending strength | 23℃ | ASTM D-790(ISO 178) | 850(84) | kg/cm2(MPa) |
| Rockwell hardness | 23℃ | ASTM D-785(ISO 2039/2) | R-110 | |
| Bending modulus | 23℃ | ASTM D-790(ISO 178) | 27000(2650) | kg/cm2(MPa) |
| tensile strength | 23℃ | ASTM D-638(ISO 527) | 530(52) | kg/cm2(MPa) |
| IZOD impact strength | 23℃1/4 | ASTM D-256 | 20 | kg.cm/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | Annealed(8℃×8hr) | ASTM D-1238(ISO 1133) | 101 | °C |
| vicat softening point | 1Kg load | ASTM D-1525(ISO R180) | 104 | °C |
| Hot deformation temperature | Unanneaied 18.6kg/cm²(1/2"厚) | ASTM D-648(ISO 75/A) | 89 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.