PA6 LUVOCOM® 3/CF/30 VP

Properties:
Filler
carbon fiber reinforced material
30%
filler by weight
Usages:
Applications in profiles
rollers
handles
engineering accessories
textile applications
and automotive fields
Compare

Technical Data Sheet

physical property	Test Method	Test Result
Water absorption rate		<1.0 %
density	ISO1183	1.28 g/cm³
Shrinkage rate	DIN16901	0.10到0.30 %

Mechanical properties	Test Condition	Test Method	Test Result
Tensile stress	Break	ISO527-2	210 MPa
Tensile strain	Yield	ISO527-2	3.0 %
Flexural modulus		ISO178	15000 MPa
Bending stress		ISO178	315 MPa
Bending Strain		ISO178	3.0 %
Tensile modulus		ISO527-2	16000 MPa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO179/1fU	45 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO179/1fU	50 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		IEC60093	<1.0E+3 ohms
insulation resistance		IEC60167	<1.0E+3 ohms

Thermal performance	Test Method	Test Result
	ISO75-2/A	210 °C
Continuous use temperature	UL746B	90.0 °C
Maximum operating temperature - SharrTerm		210 °C
	DIN53752	2E-05 cm/cm/°C
thermal conductivity	DIN52612	0.50 W/m/K

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.