AS 378PG7
0
- Properties:35%GF
CompareTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 5 cm | ||
| Water absorption rate | 0.25 % | ||
| density | 1360 Kg/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 9500 MPa | ||
| 7500 MPa | |||
| Charpy Notched Impact Strength | 17 Kj/m | ||
| 17 Kj/m | |||
| 4 Kj/m | |||
| Tensile modulus | 12000 MPa | ||
| tensile strength | 110 MPa | ||
| Tensile fracture elongation | 2 % |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | 20 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | 3.5 | ||
| 3.2 | |||
| Dissipation Factor | 70 E-4 | ||
| 100 E-4 | |||
| Volume resistivity | >1E13 Ω.m | ||
| Surface Resistivity | >1E15 Ω | ||
| dielectric strength | 39 KV/mm | ||
| Compared to the Leakage Traceability Index (CTI) | 600 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | 105 ℃ | ||
| 108 ℃ | |||
| vicat | 109 ℃ | ||
| Linear coefficient of thermal expansion | 0.25 E-4/℃ | ||
| combustibility | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.