PPA A-6135 HN BK324 SOLVAY USA

167

Form：Granules | Grade：Injection grade

Properties:

Chemical resistanceLow moisture absorption

Typical Applications:

ShellVehicle electronics

Supplier(3)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Shell \| Vehicle electronics
Properties:	Chemical resistance \| Low moisture absorption

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180	62	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D790	310	Mpa
Bending modulus	175°C	ISO 178	4600	Mpa
	Bending modulus	150°C	ISO 178	4900	Mpa
		Bending modulus	100°C	ISO 178	6600	Mpa
			Bending modulus	23°C	ISO 178	11400	Mpa
			Bending modulus	Bending modulus		ASTM D790	11400	Mpa
Tensile strain	Break,175°C	ISO 527-2	4.7	%
Tensile strain	Tensile strain	Break,150°C	ISO 527-2	4.9	%
shear strength		ASTM D732	87.6	Mpa
compressive strength		ASTM D695	148	Mpa
bending strength	3.5%Strain,175°C	ISO 178	112	Mpa
bending strength	bending strength	3.5%Strain,150°C	ISO 178	123	Mpa
Poisson's ratio			7.58	0.39
bending strength	3.5%Strain,23°C	ISO 178	300	Mpa
bending strength	bending strength	3.5%Strain,100°C	ISO 178	170	Mpa
Tensile modulus		ASTM D638	13800	Mpa
	Tensile modulus	23°C	ISO 527-2	11500	Mpa
	Tensile modulus	Tensile modulus	100°C	ISO 527-2	7310	Mpa
tensile strength	Break,24°C	ISO 527-2	121	Mpa
	tensile strength	Break,150°C	ISO 527-2	92.4	Mpa
	tensile strength	tensile strength	Break,175°C	ISO 527-2	82.0	Mpa
elongation	Break	ASTM D638	1.9	%
Tensile strain	Break,23°C	ISO 527-2	2.0	%
Tensile strain	Tensile strain	Break,24°C	ISO 527-2	4.3	%
Tensile modulus	150°C	ISO 527-2	6270	Mpa
Tensile modulus	Tensile modulus	175°C	ISO 527-2	5310	Mpa
tensile strength		ASTM D638	203	Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2	211	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：0to100°C	ASTME831	6.1E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：100to200°C	ASTME831	1.6E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：0to100°C	ASTME831	2.2E-05	cm/cm/°C
Melting temperature		ASTM D570	310	°C
Melting temperature	Melting temperature		ISO 11357-3	310	°C
Hot deformation temperature	1.8MPa,Annealed,3.20mm	ASTM D648	291	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	288	°C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	303	°C
Linear coefficient of thermal expansion	TD：100to200°C	ASTME831	1E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD	ASTM D955	0.60	%
	Shrinkage rate	TD	ASTM D955	0.90	%
		Shrinkage rate	TD	ISO 294-4	1.0	%
		Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.50	%
Water absorption rate	24hr	ASTM D570	0.30	%
Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	0.29	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	125

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PPA A-6135 HN BK324 SOLVAY USA

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index