Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.60 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.50to0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.30to0.45 % |
| Water absorption rate | | ISO 62 | 0.17 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Limiting Oxygen Index | | ASTM D2863 | 40 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| dimensional stability | | | 74.0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO 527-2/5 | 2.3 % |
| Tensile strain | | ISO 527-2/5 | 2.4 % |
| Tensile strain | | ISO 527-2/5 | 2.5 % |
| tensile strength | | ISO 527-2/5 | 125 MPa |
| tensile strength | | ISO 527-2/5 | 115 MPa |
| tensile strength | | ISO 527-2/5 | 100 MPa |
| tensile strength | | ISO 527-2/5 | 90.0 MPa |
| Tensile modulus | | ISO 527-2/1 | 9600 MPa |
| Tensile modulus | | ISO 527-2/1 | 9400 MPa |
| Tensile modulus | | ISO 527-2/1 | 9200 MPa |
| Tensile modulus | | ISO 527-2/1 | 9000 MPa |
| Tensile modulus | | ISO 527-2/1 | 8600 MPa |
| tensile strength | | ISO 527-2/5 | 130 MPa |
| Tensile strain | | ISO 527-2/5 | 2.0 % |
| Tensile strain | | ISO 527-2/5 | 2.1 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 25 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 220 °C |
| Heat distortion temperature | | ISO 75-2/A | 215 °C |
| Heat distortion temperature | | | 185 °C |
| vicat | | ISO 306/B50 | 220 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 4E-06 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.