PBT VALOX™ 357-GY2D468
183
- Properties:Flame retardantUV resistance
- Usages:Electrical appliancesPlastic bagCastersHousehold goodsSpoolShellswitch
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 1.2-1.6 % | |
| Water absorption rate | ASTM D570 | 0.080 % | |
| ISO 62 | 0.50 % | ||
| ISO 62 | 0.15 % | ||
| Outdoor applicability | UL 746C | f2 | |
| density | ASTM D792 | 1.35 g/cm³ | |
| Specific volume | ASTM D792 | 0.740 cm³/g | |
| density | ISO 1183 | 1.34 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 9.6 g/10min | |
| Melt volume flow rate | ISO 1133 | 8.00 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.80-1.1 % | |
| 内部方法 | 1.0-1.4 % | ||
| 内部方法 | 1.0-1.4 % | ||
| 内部方法 | 0.90-1.3 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 117 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | V-0 | ||
| UL 94 | 5VA | ||
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | IEC 60695-2-13 | 775 °C | |
| IEC 60695-2-13 | 750 °C | ||
| IEC 60695-2-13 | 725 °C | ||
| Limiting Oxygen Index | ASTM D2863 | 30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2/50 | 40.0 Mpa | |
| Tensile strain | ASTM D638 | 5.0 % | |
| ISO 527-2/50 | 5.0 % | ||
| ASTM D638 | 54 % | ||
| ISO 527-2/50 | 30 % | ||
| Flexural modulus | ASTM D790 | 2100 Mpa | |
| ISO 178 | 2000 Mpa | ||
| bending strength | ISO 178 | 73.0 Mpa | |
| ASTM D790 | 78.0 Mpa | ||
| ASTM D790 | 78.0 Mpa | ||
| Tensile modulus | ASTM D638 | 2020 Mpa | |
| ISO 527-2/1 | 2200 Mpa | ||
| tensile strength | ASTM D638 | 48.0 Mpa | |
| ISO 527-2/50 | 50.0 Mpa | ||
| ASTM D638 | 42.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 45 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 150 J/m | |
| ASTM D256 | 320 J/m | ||
| ISO 180/1A | 10 kJ/m² | ||
| ISO 180/1A | 45 kJ/m² | ||
| ASTM D4812 | NoBreak | ||
| Dart impact | ASTM D3763 | 35.8 J | |
| ASTM D3029 | 43.4 J | ||
| ASTM D3029 | 43.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.2E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 25 KV/mm | |
| ASTM D149 | 19 KV/mm | ||
| ASTM D149 | 19 KV/mm | ||
| dielectric constant | ASTM D150 | 3.20 | |
| ASTM D150 | 3.20 | ||
| Dissipation Factor | ASTM D150 | 3E-03 | |
| ASTM D150 | 0.030 | ||
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 3 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 3 | |
| Hot wire ignition (HWI) | UL 746 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 135 °C | |
| ASTM D648 | 138 °C | ||
| ASTM D648 | 98.0 °C | ||
| ASTM D648 | 99.0 °C | ||
| ISO 75-2/Af | 84.0 °C | ||
| vicat | ASTM D152513 | 134 °C | |
| ISO 306/B50 | 145 °C | ||
| ISO 306/B120 | 150 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | ASTME831 | 9.2E-05 cm/cm/°C | |
| ASTME831 | 1.2E-04 cm/cm/°C | ||
| ISO 11359-2 | 7.2E-05 cm/cm/°C | ||
| ASTME831 | 8.4E-05 cm/cm/°C | ||
| ISO 11359-2 | 8.4E-05 cm/cm/°C | ||
| RTI Elec | UL 746 | 120 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI Str | UL 746 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.