PP Homopolymer Polifil® PP C-30
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.15 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 8.0to12 g/10min | |
| Shrinkage rate | ASTM D955 | 1.2 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hardness (Shore) | ASTM D1415 | 75 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ASTM D638 | 40 % | |
| Flexural modulus | ASTM D790 | 2070 MPa | |
| bending strength | ASTM D790 | 41.4 MPa | |
| Tensile modulus | ASTM D638 | 1860 MPa | |
| tensile strength | ASTM D638 | 26.2 MPa | |
| elongation | ASTM D638 | 6.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 40 J/m | |
| Dart impact | ASTM D3029 | 6.78 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ASTM D648 | 104 °C | |
| ASTM D648 | 60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.