PC R-FR610
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.18 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.60 % | |
| ISO 294-4 | 0.60 % | ||
| Water absorption rate | ISO 62 | 0.50 % | |
| ISO 62 | 0.20 % | ||
| melt mass-flow rate | ISO 1133 | 20 cm³/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/1A | 10 kJ/m² | |
| tensile strength | ISO 527-2 | 55 MPa | |
| elongation at break | ISO 527-2 | 30 % | |
| Tensile modulus | ISO 527-2 | 2600 MPa | |
| Impact strength of cantilever beam gap | ISO 180/1A | 40 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | 1.00mm | |
| UL -94 | V-0 1.50mm | ||
| UL -94 | V-0.5VA 3.00mm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+16 Ω.cm | |
| Surface Resistivity | IEC 60093 | 1E+16 Ω.cm | |
| dielectric strength | IEC 60243-1 | 30 KV/mm | |
| dielectric constant | IEC 60250 | 3.10 1MHz | |
| Dissipation Factor | IEC 60250 | 8.5E-03 1MHz | |
| IEC 60112 | 300 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Bf | 95 °C | |
| ISO 75-2/Af | 85 °C | ||
| vicat | ISO 306/B50 | 108 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 7.6E-05 cm/cm／°C | |
| ISO 11359-2 | 8E-05 cm/cm／°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.