ASA HRA222 SABIC INNOVATIVE US

191

Form：Granules | Grade：Injection grade

Properties:

UV resistanceFlame retardant

Typical Applications:

Electrical appliancesElectronic fieldElectrical field

Supplier(2)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Electrical appliances \| Electronic field \| Electrical field
Properties:	UV resistance \| Flame retardant

Certificates

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8 mm	UL 94	V-2
	UL flame retardant rating	2.0 mm	UL 94	V-0
		UL flame retardant rating	2.3 mm	UL 94	5VB
		UL flame retardant rating	UL flame retardant rating	2.3 mm	UL 94	5VB
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960	°C
Extreme Oxygen Index		ISO 4589-2	29	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--3	ASTM D638	2590	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2520	Mpa
tensile strength	Yield4	ASTM D638	63.0	Mpa
	tensile strength	Yield5	ASTM D638	59.0	Mpa
		tensile strength	Yield	ISO 527-2/5	62.0	Mpa
			tensile strength	Yield	ISO 527-2/50	60.0	Mpa
				tensile strength	Break5	ASTM D638	66.0	Mpa
					tensile strength	Break4	ASTM D638	56.0	Mpa
						tensile strength	Break	ISO 527-2/5	51.0	Mpa
						tensile strength	tensile strength	Break	ISO 527-2/50	45.0	Mpa
elongation	Yield5	ASTM D638	4.2	%
	elongation	Yield4	ASTM D638	4.3	%
		elongation	Yield	ISO 527-2/5	4.3	%
			elongation	Yield	ISO 527-2/50	4.4	%
				elongation	Break5	ASTM D638	> 100	%
					elongation	Break4	ASTM D638	> 100	%
					elongation	elongation	Break	ISO 527-2/5	> 50	%
Bending modulus		ISO 178	2510	Mpa
bending strength		ISO 178	93.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80 to 90	°C
drying time			2.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Hopper temperature			60 to 80	°C
Temperature at the rear of the barrel			200 to 230	°C
Temperature in the middle of the barrel			220 to 260	°C
Temperature at the front of the material cylinder			230 to 270	°C
Spray nozzle temperature			220 to 260	°C
Processing (melt) temperature			230 to 270	°C
Mold temperature			50 to 70	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	99.0	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	88.0	°C
Vicat softening temperature	--	ISO 306/A50	111	°C
	Vicat softening temperature	--	ISO 306/B50	102	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	104	°C
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -30 to 80°C	ISO 11359-2	6.9E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -30 to 80°C	ISO 11359-2	7.1E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.5E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	13.0	cm3/10min
Shrinkage rate	Flow	Internal Method	0.40 - 0.60	%
Water absorption rate	Saturation, 23°C	ISO 62	0.60	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.20	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

ASA HRA222 SABIC INNOVATIVE US

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index