Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | 内部方法 | 1.51 g/cm³ |
| Shrinkage rate | | 内部方法 | 0.25 % |
| Shrinkage rate | | 内部方法 | 0.75 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | 内部方法 | 100 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | 内部方法 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | 内部方法 | 120 MPa |
| elongation | Break | 内部方法 | 1.8 % |
| Flexural modulus | | 内部方法 | 11500 MPa |
| bending strength | | 内部方法 | 172 MPa |
| compressive strength | | 内部方法 | 137 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | 内部方法 | 11 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | 内部方法 | 6.9E+15 ohms |
| Volume resistivity | | 内部方法 | 1.4E+17 ohms·cm |
| dielectric strength | | 内部方法 | 17 kV/mm |
| dielectric constant | | 内部方法 | 4.00 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | 内部方法 | 264 °C |
| melting temperature | | 内部方法 | 281 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare