PA66 A3 GF 25 1 NA AKRO-PLASTIC GERMANY

Form：Granules

Properties:

Thermal stabilityGlass fiber reinforcedHigh rigidityenhancehigh strength

Typical Applications:

Industrial machineryIndustrial applicationsAutomotive sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Industrial machinery \| Industrial applications \| Automotive sector
Properties:	Thermal stability \| Glass fiber reinforced \| High rigidity \| enhance \| high strength

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	64	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	70	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	FMVSS302	<100	mm/min
UL flame retardant rating	0.8mm	UL 94	HB
Burning wire flammability index	1.6mm	IEC 60695-2-12	650	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	8500	Mpa
tensile strength	Break	ISO 527-2/5	185	Mpa
Tensile strain	Break	ISO 527-2/5	3.6	%
Bending modulus		ISO 178	7600	Mpa
bending strength		ISO 178	260	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	260	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	255	°C
Melting temperature		DIN EN11357-1	262	°C
TemperatureIndex	50%LossofTensileStrength,20000hr	IEC 216	130to150	°C
TemperatureIndex	TemperatureIndex	50%LossofTensileStrength,5000hr	IEC 216	160to175	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD	ISO 294-4	0.20	%
Water absorption rate	Saturation,23°C	ISO 62	5.7to6.3	%
Hygroscopicity	70°C，62%RH	ISO 1110	2.0to2.2	%
Spiral flow length		Internal Method	89.0	CM
Shrinkage rate	TD	ISO 294-4	1.3	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+12	ohms
Volume resistivity		IEC 60093	1E+13	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H961/30	ISO 2039-1	225	Mpa
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ReinforcementContent		ISO 1172	25	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.