'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC HFD4413-BK1E711 SABIC INNOVATIVE NANSHA
97
Form：Granules
Properties:
High mobilityHydrolysis resistance
Typical Applications:
Electrical applicationsAutomotive ApplicationsMechanical accessories
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Electrical applications | Automotive Applications | Mechanical accessories |
| Properties: | High mobility | Hydrolysis resistance |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 | kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 850 | J/m |
| -30°C7 | ISO 180/1U | 30 | kJ/m² | |
| 23°C7 | ISO 180/1U | 37 | kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 17.0 | J |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 49 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 | kJ/m² |
| -30°C | ISO 179/1eA | 11 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 850 | °C |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 | °C |
| UL flame retardant rating | 0.8mm | UL 94 | HB | |
| 0.30mm | UL 94 | HB | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | Yield4 | ASTM D638 | 111 | Mpa |
| Tensile modulus | ASTM D638 | 7870 | Mpa | |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 182 | Mpa |
| Bending modulus | 50.0mmSpan | ASTM D790 | 7760 | Mpa |
| elongation | Break | ISO 527-2/5 | 2.1 | % |
| Yield | ISO 527-2/5 | 2.5 | % | |
| Yield4 | ASTM D638 | 3.0 | % | |
| tensile strength | Break | ISO 527-2/5 | 125 | Mpa |
| Break4 | ASTM D638 | 111 | Mpa | |
| Yield | ISO 527-2/5 | 115 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| RTI | UL 746 | 80.0 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTM D648 | 130 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTM D648 | 125 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan8 | ISO 75-2/Af | 129 | °C | |
| Vicat softening temperature | ISO 306/B120 | 143 | °C | |
| Ball Pressure Test | 125°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831 | 3E-05 | cm/cm/°C |
| MD:23to80°C | ISO 11359-2 | 3E-05 | cm/cm/°C | |
| TD:-40to40°C | ASTME831 | 7E-05 | cm/cm/°C | |
| TD:23to80°C | ISO 11359-2 | 7E-05 | cm/cm/°C | |
| RTI Elec | UL 746 | 80.0 | °C | |
| RTI Imp | UL 746 | 80.0 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.12 | % |
| Saturation,23°C | ISO 62 | 0.30 | % | |
| Shrinkage rate | TD:3.20mm | Internal Method | 0.10-0.30 | % |
| MD:3.20mm | Internal Method | 0.10-0.30 | % | |
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 18.0 | cm3/10min |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 16 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.