Technical Data Sheet
thermosetting | Test Condition | Test Method | Test Result |
---|
Thermosetting components | Resin | | 按重量计算的混合比:100按容量计算的混合比:7.1 |
Thermosetting components | Hardener | | 按重量计算的混合比:11按容量计算的混合比:1.0 |
Thermosetting components | | | 45to55 min |
Thermosetting mixed viscosity | | ASTM D2393 | 4500 cP |
physical property | Test Condition | Test Method | Test Result |
---|
Apparent density | | ASTM D1895 | 1.30 g/cm³ |
hardness | Test Condition | Test Method | Test Result |
---|
Shore hardness | | ASTM D2240 | 92 |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
compressive strength | | ASTM D695 | 200 MPa |
tensile strength | Break | ASTM D638 | 172 MPa |
Flexural modulus | | ASTM D790 | 11700 MPa |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Glass Transition Temperature | | ASTME1356 | 160 °C |
Linear coefficient of thermal expansion | | ASTM D696 | 2.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.