Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 3.8 g/10min |
| Environmental stress cracking resistance | | ASTM D1693 | >1000 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 49 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 0.903 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 3.8 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO 527-2 | >16 MPa |
| Tensile strain | | ISO 527-2 | >500 % |
| Impact strength of simply supported beam without notch | | ISO 179 | No Break |
| Shore hardness | | ISO 868 | 49 |
| tensile strength | | ISO 527-2 | >16.0 Mpa |
| Tensile strain | | ISO 527-2 | >500 % |
| Flexural modulus | | ISO 178 | 120 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306 | 83 ℃ |
| melting temperature | | ISO 11357-3 | 98 ℃ |
| vicat | | ISO 306 | 83.0 °C |
| melting temperature | | ISO 11357-3 | 98.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.