Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 35to45 g/10min |
| Shrinkage rate | | ASTM D955 | <0.50 % |
| Water absorption rate | | ASTM D570 | <0.20 % |
| density | | ASTM D792 | 1.28 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 86 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 3450 MPa |
| tensile strength | | ASTM D638 | 6.96 MPa |
| tensile strength | | ASTM D638 | 9.51 MPa |
| tensile strength | | ASTM D638 | 10.5 MPa |
| tensile strength | | ASTM D638 | 11.9 MPa |
| tensile strength | | ASTM D638 | 17.9 MPa |
| coefficient of friction | Itself - Static | ASTM D1894 | 0.29 |
| tensile strength | Break | ASTM D638 | 89.6 MPa |
| elongation | Break | ASTM D638 | 80 % |
| Flexural modulus | | ASTM D790 | 3380 MPa |
| bending strength | Yield | ASTM D790 | 138 MPa |
| compressive strength | | ASTM D695 | 103 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 48 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTM D150 | 1E-03 |
| dielectric constant | | ASTM D150 | 2.10 |
| Surface Resistivity | | ASTM D257 | 2E+16 ohms |
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 75 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 141 °C |
| Glass Transition Temperature | | DSC | 154 °C |
| melting temperature | | DSC | 303 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 7.7E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.25 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.