AES+PC LNP™ LUBRILOY™ Lexan_WR6300 compound SABIC

Properties:
Thermal performance
Usages:
Business equipment
Compare

Technical Data Sheet

	Test Condition	Test Method	Test Result
RTI Str		UL746	80.0 °C
UL阻燃等级	1.5mm	UL94	HB
收缩率	MD：3.20mm	内部方法	0.50to0.70 %
抗张强度	Yield	ASTMD638	60.7 MPa
抗张强度	抗张强度	Break	ASTMD638	61.4 MPa
伸长率	Break	ASTMD638	160 %
弯曲模量	50.0mm跨距	ASTMD790	2490 MPa
密度		ASTMD792	1.17 g/cm³
熔体体积流动速率	300°C/2.16kg	ISO1133	38.0 cm³/10min
线性热膨胀系数	TD：-40到40°C	ASTME831	1.2E-04 cm/cm/°C
RTI Elec		UL746	80.0 °C
RTI Imp		UL746	80.0 °C
收缩率	MD：3.20mm	内部方法	0.50到0.70 %
抗张强度	Yield	ASTMD638	60.7 MPa
弯曲强度	屈服,50.0mm跨距	ASTMD790	96.5 MPa
悬壁梁缺口冲击强度	-30°C	ASTMD256	170 J/m
	悬壁梁缺口冲击强度	23°C	ASTMD256	680 J/m
	悬壁梁缺口冲击强度	悬壁梁缺口冲击强度	23°C	ASTMD4812	2500 J/m
装有测量仪表的落镖冲击	23°C,TotalEnergy	ASTMD3763	60.2 J
热变形温度	0.45MPa,未退火,6.40mm	ASTMD648	134 °C
	热变形温度	1.8MPa,未退火,3.20mm	ASTMD648	117 °C
	热变形温度	热变形温度	1.8MPa,未退火,6.40mm	ASTMD648	121 °C
维卡软化温度		ASTMD15254	137 °C
线性热膨胀系数	MD：-40到40°C	ASTME831	1.1E-04 cm/cm/°C
弯曲强度	屈服,50.0mm跨距	ASTMD790	96.5 MPa
悬壁梁缺口冲击强度	-30°C	ASTMD256	170 J/m
悬壁梁缺口冲击强度	悬壁梁缺口冲击强度	23°C	ASTMD256	680 J/m
悬壁梁无缺口冲击强度	23°C	ASTMD4812	2500 J/m
装有测量仪表的落镖冲击	23°C,TotalEnergy	ASTMD3763	60.2 J
热变形温度	0.45MPa,未退火,6.40mm	ASTMD648	134 °C
	热变形温度	1.8MPa,未退火,3.20mm	ASTMD648	117 °C
	热变形温度	热变形温度	1.8MPa,未退火,6.40mm	ASTMD648	121 °C
维卡软化温度		ASTMD15255	137 °C
线性热膨胀系数	MD:-40到40°C	ASTME831	1.1E-04 cm/cm/°C
抗张强度	Break	ASTMD638	61.4 MPa
伸长率	Break	ASTMD638	160 %
弯曲模量	50.0mm跨距	ASTMD790	2490 MPa
线性热膨胀系数	TD:-40到40°C	ASTME831	1.2E-04 cm/cm/°C
RTI Elec		UL746	80.0 °C
RTI Imp		UL746	80.0 °C
RTI		UL746	80.0 °C
UL阻燃等级	1.50mm	UL94	HB
密度		ASTMD792	1.17 g/cm³
熔体体积流动速率	300°C/2.16kg	ISO1133	38.0 cm³/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.