Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.34 g/cm³ |
| Shrinkage rate | | | 0.30到0.40 % |
| water content | | ISO62 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO2039-2 | 112 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO527-2 | 2.3 % |
| Flexural modulus | | ISO178 | 5500 MPa |
| Bending stress | | ISO178 | 135 MPa |
| Tensile stress | Break | ISO527-2 | 105 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180 | 12 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | 1E+14 ohms |
| dielectric strength | | ASTMD149 | 16 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | | ISO75-2/B | 150 °C |
| Heat Deflection Temperature | | ISO75-2/A | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.