EVA UE631
0
- Usages:Sole foam extrusionfilm extrusion
CompareTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D-1505 | 0.942 g/cm3 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D-1709 | 374 G/F50 |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Casting film forming | ASTM D-638/D-882 | 180 kg/cm2 | |
| Shore hardness | ASTM D-2240 | 36 Shore D | |
| Low temperature brittleness temperature | ASTM D-746 | <-76 ℃/F50 | |
| emit | ASTM D-638/D-882 | 250 % | |
| Vinyl acetate content | ASTM USIFE | 22 % | |
| film thickness | ASTM D-638/D-882 | 264 kg/cm2 | |
| ASTM D-638/D-882 | 189 kg/cm2 | ||
| ASTM D-638/D-882 | 640 % | ||
| melt mass-flow rate | ASTM D-1238 | 1.4 g/10min | |
| vicat | ASTM D-1525 | 64 ℃ | |
| melting temperature | ASTM D-2117 | 82 ℃ | |
| emit | ASTM D-638/D-882 | 110 kg/cm2 | |
| film thickness | ASTM D-638/D-882 | 480 % | |
| Casting film forming | ASTM D-638/D-882 | 800 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.