PA66/PTFE Grilon® TSG30-4 LF15 EMS-CHEMIE SWITZERLAND
137
- Properties:Glass fiber reinforcedThermal stability
- Usages:Automotive ApplicationsProfile
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 干燥｜0.70 % | |
| ISO 294-4 | 干燥｜0.20 % | ||
| Water absorption rate | ISO 62 | 干燥｜4.0 % | |
| ISO 62 | 干燥｜1.5 % |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flammability level | IEC 60695-11-10, -20 | 干燥｜V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 2039-1 | 干燥｜255 Mpa | ||
| ISO 2039-1 | 调节后｜130 Mpa | ||
| Tensile modulus | ISO 527-2 | 干燥｜10500 Mpa | |
| ISO 527-2 | 调节后｜6500 Mpa | ||
| Tensile stress | ISO 527-2 | 干燥｜150 Mpa | |
| ISO 527-2 | 调节后｜90.0 Mpa | ||
| Tensile strain | ISO 527-2 | 干燥｜2.5 % | |
| ISO 527-2 | 调节后｜4.5 % | ||
| Charpy Notched Impact Strength | ISO 179/1eA | 干燥｜9.0 kJ/m² | |
| ISO 179/1eA | 调节后｜8.5 kJ/m² | ||
| ISO 179/1eA | 干燥｜9.5 kJ/m² | ||
| ISO 179/1eA | 调节后｜14 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 干燥｜60 kJ/m² | |
| ISO 179/1eU | 调节后｜60 kJ/m² | ||
| ISO 179/1eU | 干燥｜65 kJ/m² | ||
| ISO 179/1eU | 调节后｜70 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 调节后｜1.0E+12 ohms·cm | |
| dielectric strength | IEC 60243-1 | 干燥｜28 KV/mm | |
| IEC 60243-1 | 调节后｜26 KV/mm | ||
| CTI | IEC 60112 | 调节后｜600 V | |
| Surface Resistivity | IEC 60093 | 调节后｜1.0E+10 ohms | |
| Volume resistivity | IEC 60093 | 干燥｜1.0E+12 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 75-2/A | 干燥｜235 °C | ||
| ISO 75-2/C | 干燥｜165 °C | ||
| Continuous use temperature | ISO 2578 | 干燥｜100 到120 °C | |
| 内部方法 | 干燥｜220 °C | ||
| Melting temperature 5 | ISO 11357-3 | 干燥｜260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.