Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO1133 | 5.50 cm3/10min |
| Shrinkage rate | | ISO294-4 | 0.40到0.70 % |
| Water absorption rate | | ISO62 | <0.10 % |
| Water absorption rate | | ISO62 | <0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 83.0 Mpa |
| other | Test Condition | Test Method | Test Result |
|---|
| colour | | | 本色 |
| purpose | | | IT办公 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Gardner glossiness | | ASTMD523 | 70 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 2050 Mpa |
| Tensile stress | | ISO527-2 | 30.0 Mpa |
| Tensile strain | | ISO527-2 | 1.6 % |
| Tensile strain | | ISO527-2 | 30 % |
| Flexural modulus | | ISO178 | 2100 Mpa |
| Bending stress | | ISO178 | 44.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 70 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 120 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | >1.0E+13 ohms |
| Volume resistivity | | IEC60093 | >1.0E+18 ohms·cm |
| Dielectric strength 4 | | IEC60243-1 | 160 KV/mm |
| dielectric constant | | IEC60250 | 2.50 |
| dielectric constant | | IEC60250 | 2.50 |
| Dissipation Factor | | IEC60250 | 4E-04 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature 3 | | ISO75-2/B | 88.0 °C |
| Hot deformation temperature 3 | | ISO75-2/A | 78.0 °C |
| vicat | | ISO306/A50 | 98.0 °C |
| vicat | | ISO306/B50 | 90.0 °C |
| | ISO11359-2 | 1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare