Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.04 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 50 g/10min |
| melt mass-flow rate | | ASTMD1238 | 5.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 104 |
| Rockwell hardness | | ISO 2039-2 | 104 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 2350 MPa |
| tensile strength | | ASTMD638 | 40.0 MPa |
| bending strength | | ASTMD790 | 68.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 290 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 88.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 88.0 °C |
| Heat distortion temperature | | ASTM D648 | 100 °C |
| Heat distortion temperature | | ISO 75-2/A | 100 °C |
| vicat | | ISO 306/A | 103 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.