Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ISO60 | 0.60 g/cm³ |
| Shrinkage rate | | ISO294-4 | 0.81 % |
| Shrinkage rate | | ISO294-4 | 0.10 % |
| Shrinkage rate | | ISO294-4 | 0.29 % |
| Shrinkage rate | | ISO294-4 | 0.050 % |
| Water absorption rate | | ISO62 | 7.0 % |
| Water absorption rate | | ISO62 | 2.1 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 193 Mpa |
| other | Test Condition | Test Method | Test Result |
|---|
| | | 耐气候影响性能良好 热稳定性 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| BurningBehavior9 | | ISO3795 | passed |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISO Shortcut | | ISO1874 | PA6,GHR,10-090,GF30 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 8730 Mpa |
| Tensile modulus | | ISO527-2/1 | 9400 Mpa |
| tensile strength | | ASTMD638 | 165 Mpa |
| Tensile stress | | ISO527-2/5 | 170 Mpa |
| elongation | | ASTMD638 | 3.2 % |
| Tensile strain | | ISO527-2/5 | 3.0 % |
| Flexural modulus | | ASTMD790 | 8000 Mpa |
| Flexural modulus | | ISO178/A | 8400 Mpa |
| bending strength | | ASTMD790 | 260 Mpa |
| Bending stress | | ISO178/A | 255 Mpa |
| Bending stress | | ISO178 | 260 Mpa |
| Bending stress | | | 3.6 % |
| Tensile modulus | | ASTM D638/ISO 527 | 9910 kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ASTM D638/ISO 527 | 175 kg/cm²(MPa)[Lb/in²] |
| Flexural modulus | | ASTM D790/ISO 178 | 9120 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 276 kg/cm²(MPa)[Lb/in²] |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| | ISO180/1U | 60 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 55 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 65 kJ/m² |
| | ISO180/1U | 55 kJ/m² |
| film | Test Condition | Test Method | Test Result |
|---|
| | ISO6603-2 | 2.10 J |
| | ISO6603-2 | 2.20 J |
| | ISO6603-2 | 744 N |
| | ISO6603-2 | 803 N |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC60243-1 | 33 KV/mm |
| CTI | | IEC60112 | 400 V |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.36 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 219 °C |
| | ISO75-2/A | 210 °C |
| | ISO75-2/C | 150 °C |
| vicat | | ISO306/B120 | 210 °C |
| BallPressure Test | | IEC60695-10-2 | Pass |
| Melting temperature 5 | | ISO11357-3 | 221 °C |
| | ISO11359-2 | 2E-05 cm/cm/°C |
| | ISO11359-2 | 1E-04 cm/cm/°C |
| Combustibility (rate) | | UL94 | HB |
| vicat | | ASTM D1525/ISO R306 | 210 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.