SMMA NAS® 30 INEOS Barex
0
- Properties:physical property
CompareTechnical Data Sheet
| Test Condition | Test Method | Test Result | |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 2.2 g/10min | |
| Melt volume flow rate | ISO 1133 | 30.0 cm³/10min | |
| transmissivity | ASTM D1003 | 91.4 % | |
| Haze ratio | ASTM D1003 | 0.30 % | |
| Shrinkage rate | ASTM D955 | 0.20to0.60 % | |
| ISO 294-4 | 0.20to0.60 % | ||
| Water absorption rate | ASTM D570 | 0.15 % | |
| ISO 62 | 0.15 % | ||
| Tensile modulus | ASTM D638 | 3240 MPa | |
| ISO 527-2 | 3300 MPa | ||
| tensile strength | ASTM D638 | 60.7 MPa | |
| ISO 527-2 | 60.0 MPa | ||
| elongation | Break | ASTM D638 | 2.3 % |
| Tensile strain | ISO 527-2 | 2.5 % | |
| Flexural modulus | ASTM D790 | 3170 MPa | |
| Charpy Notched Impact Strength | ISO 179 | 1.5 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179 | 12 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 21 J/m | |
| ISO 180/A | 2.5 kJ/m² | ||
| density | ASTM D792 | 1.09 g/cm³ | |
| ISO 1183 | 1.09 g/cm³ | ||
| Suspended wall beam without notch impact strength | ISO 180 | 12 kJ/m² | |
| Rockwell hardness | M-Scale | ASTM D785 | 75 |
| ball-indentation hardness | ISO 2039-1 | 169 MPa | |
| Heat distortion temperature | ISO 75-2/B | 90.0 °C | |
| ISO 75-2/A | 80.0 °C | ||
| vicat | ASTM D15253 | 104 °C | |
| ISO 306/B50 | 98.0 °C | ||
| Flexural modulus | ISO 178 | 3400 MPa | |
| bending strength | ASTM D790 | 101 MPa | |
| ISO 178 | 100 MPa | ||
| maximum service temperature | 260 °C | ||
| refractive index | ASTM D542 | 1.560 | |
| ISO 489 | 1.560 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.