Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.26 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 14 g/10min |
| Melt volume flow rate | | ISO 1133 | 13.8 cm³/10min |
| Water absorption rate | | ISO 62 | 0.60 % |
| Water absorption rate | | ISO 62 | 0.25 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 55 |
| Shore hardness | | ISO 868 | 55 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | | IEC 60695-11-10,-20 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 24.0 MPa |
| Tensile modulus | | ISO 527-2 | 200 MPa |
| tensile strength | | ISO 527-2 | 13.4 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 6.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.6E-04 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/B | 80.0 °C |
| vicat | | ISO 306/B50 | 85.0 °C |
| melting temperature | | ISO 11357-3 | 200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.