ULDPE NG 4701G
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 0.912 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 0.80 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D2457 | 49 | |
| Haze ratio | ASTM D1003 | 11 % |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| film strength | ASTM D882 | 70.3 J/cm³ | |
| Secant modulus | ASTM D882 | 141 MPa | |
| ASTM D882 | 124 MPa | ||
| ASTM D882 | 131 MPa | ||
| tensile strength | ASTM D882 | 8.96 MPa | |
| ASTM D882 | 8.62 MPa | ||
| ASTM D882 | 41.4 MPa | ||
| ASTM D882 | 37.2 MPa | ||
| elongation | ASTM D882 | 400 % | |
| ASTM D882 | 450 % | ||
| Dart impact | ASTM D1709B | 380 g | |
| Elmendorf tear strength | ASTM D1922 | 250 g | |
| Thin film puncture strength | 内部方法 | 6.21 J | |
| 内部方法 | 71.2 N | ||
| 内部方法 | 33.1 J/cm³ | ||
| film strength | ASTM D882 | 72.8 J/cm³ | |
| Elmendorf tear strength | ASTM D1922 | 600 g | |
| Secant modulus | ASTM D882 | 148 MPa | |
| film thickness | 25 µm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM D1525 | 99.0 °C | |
| melting temperature | ISO 3146 | 101 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.