PEEK 770GL20 JILIN JOINATURE

Form：Granules | Grade：Injection grade

Properties:

enhanceGlass fiber reinforcedstandard

Typical Applications:

AerospaceElectrical fieldElectronic fieldElectric wireCableIndustrial machineryMedical suppliesNursing suppliesAutomotive sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Aerospace \| Electrical field \| Electronic field \| Electric wire \| Cable \| Industrial machinery \| Medical supplies \| Nursing supplies \| Automotive sector
Properties:	enhance \| Glass fiber reinforced \| standard

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap		ISO 180/A	7.5	kJ/m²
Suspended wall beam without notch impact strength		ISO 180/U	60	kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1U	45	kJ/m²
Charpy Notched Impact Strength		ISO 179-1eA	7	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	23℃	ISO 868	85	D 级
compressive strength	23℃	ISO 604	-	Mpa
Tensile strain	Break，23℃	ISO 527	3.3	%
Bending modulus	23℃	ISO 178	8800	Mpa
bending strength	Break，23℃	ISO 178	245	Mpa
tensile strength	Break，23℃	ISO 527	155	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
thermal conductivity	23℃	ISO 22007-4	0.3	W/m/K
Melting temperature		ISO 11357	343	°C
Tg (initial)		ISO 11357	143	°C
specific heat	23℃	DSC	1.7	kJ/kg /℃
Linear coefficient of thermal expansion	低于Tg沿着Flow	ISO 11359	20	ppm/K
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	高于Tg沿着Flow	ISO 11359	22	ppm/K
Hot deformation temperature	1.8 Mpa	ISO 75-f	315	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23℃，24hr，3.2 mm厚拉伸棒	ISO 62-1	0.05	%
Water absorption rate	Water absorption rate	Equilibrium，23℃	ISO 62-1	0.4	%
Shrinkage rate	MD	ISO 294-4	0.8	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.3	%
melt mass-flow rate	380℃，5.0kg	ISO 1133	6.5	g/10min
density	结晶	ISO 1183	1.43	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	23℃，1 MHz	IEC 60250	0.005
Dielectric constant	23 ℃, 1 kHz	IEC 60250	3.1
Compared to the anti leakage trace index		IEC 60112	PLC 4
Dielectric strength	2 mm	IEC 60243-1	24	KV/mm
Volume resistivity	23 ℃，1V	IEC 60093	10^16	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.