PA6 BU50I BASF GERMANY

Form：Granules | Grade：Injection grade

Properties:

Oil resistantHigh impact resistance

Typical Applications:

Electrical enclosurefilmEngineering accessories

Supplier(0)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Electrical enclosure \| film \| Engineering accessories
Properties:	Oil resistant \| High impact resistance

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			超高韧性耐低温抗撞击性
purpose			汽车领域应用体育用品安全帽
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
Dart impact	23°C	Internal Method	8.67	J/cm
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break		ASTM D638/ISO 527	40	%
Tensile modulus		ASTM D638/ISO 527	1600	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	1690	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	65	kg/cm²(MPa)[Lb/in²]
	bending strength	23°C	ASTM D790	65.0	Mpa
	bending strength	bending strength	23°C	ISO 178	50.0	Mpa
Tensile modulus	23°C	ISO 527-2	1600	Mpa
tensile strength	Yield,23°C	ASTM D638	50.0	Mpa
	tensile strength	Yield,23°C	ISO 527-2	45.0	Mpa
	tensile strength	tensile strength	Break,23°C	ASTM D638	45.0	Mpa
elongation	Yield,23°C	ASTM D638	5.0	%
Tensile strain	Yield,23°C	ISO 527-2	4.0	%
elongation	Break,23°C	ASTM D638	>100	%
Nominal tensile fracture strain	23°C	ISO 527-2	40	%
Bending modulus	23°C	ASTM D790	1690	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	1550	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	HB
Melting temperature		ASTM D3418	220	°C
Melting temperature	Melting temperature		ISO 3146	220	°C
RTI Elec	0.8mm	UL 746	65.0	°C
	RTI Elec	1.5mm	UL 746	65.0	°C
	RTI Elec	RTI Elec	3.0mm	UL 746	65.0	°C
RTI Imp	0.8mm	UL 746	65.0	°C
	RTI Imp	1.5mm	UL 746	65.0	°C
	RTI Imp	RTI Imp	3.0mm	UL 746	65.0	°C
RTI Str	0.8mm	UL 746	65.0	°C
RTI Str	RTI Str	1.5mm	UL 746	65.0	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	60.0	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	50.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	50.0	°C
RTI Str	3.0mm	UL 746	65.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.06
Shrinkage rate	MD：3.18mm		1.8	%
Water absorption rate	Saturation	ASTM D570	7.3	%
	Water absorption rate	Saturation,23°C	ISO 62	7.3	%
		Water absorption rate	Equilibrium,50%RH	ASTM D570	2.1	%
		Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.1	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.