PA66 A 20 V25 TECNICA ITALY

Form：Granules | Grade：Enhanced level

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	50	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	55	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8 mm	UL 94	V-0
	UL flame retardant rating	1.6 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.2 mm	UL 94	V-0
Burning wire flammability index	0.8 mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	1.6 mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	3.2 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.6 mm	IEC 60695-2-13	725	°C
Extreme Oxygen Index		ISO 4589-2	31	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2/1A	9400	Mpa
tensile strength	Break, 23°C	ISO 527-2/1A	150	Mpa
Tensile strain	Break, 23°C	ISO 527-2	2.5	%
Bending modulus	23°C	ISO 178	8500	Mpa
bending strength	23°C	ISO 178	255	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
Suggested maximum moisture content			0.20	%
Temperature at the rear of the barrel			265 to 275	°C
Temperature in the middle of the barrel			270 to 280	°C
Temperature at the front of the material cylinder			280 to 290	°C
Mold temperature			60 to 90	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	244	°C
Melting temperature		ISO 11357-3	263	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	横向Flow	ISO 294-4	1.2	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.35	%
Water absorption rate	24 hr, 23°C	ISO 62	0.75	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.1	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1.0E+13	ohms
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength	0.800 mm	IEC 60243-1	30	KV/mm
Relative permittivity		IEC 60250	3.40
Dissipation factor		IEC 60250	0.020
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App