'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPA HTNFR51G35L NC010 DUPONT JAPAN
173
Form：Granules
Properties:
Glass fiber reinforcedThermal stabilityHigh temperature resistanHydrolysis resistance
Typical Applications:
Automotive interior partsFitness equipmentelectrical equipment
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Automotive interior parts | Fitness equipment | electrical equipment |
| Properties: | Glass fiber reinforced | Thermal stability | High temperature resistan | Hydrolysis resistance |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 | kJ/m² |
| -30°C | ISO 179/1eU | 60 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| FMVSS flammability | FMVSS302 | B | ||
| Extreme Oxygen Index | ISO 4589-2 | 24 | % | |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB | |
| 0.9mm | IEC 60695-11-10,-20 | HB | ||
| 1.5mm | UL 94 | HB | ||
| 0.9mm | UL 94 | HB | ||
| Burning rate | 1.00mm | ISO 3795 | 23 | mm/min |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Poisson's ratio | ISO 527 | 0.39 | ||
| bending strength | ISO 178 | 300 | Mpa | |
| Tensile strain | Break | ISO 527-2 | 2.4 | % |
| tensile strength | Break | ISO 527-2 | 210 | Mpa |
| Tensile modulus | ISO 527-2 | 12000 | Mpa | |
| Bending modulus | ISO 178 | 10300 | Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | -- | Mpa |
| 1hr | ISO 899-1 | -- | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Melting temperature | ISO 11357-3 | 300 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 260 | °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 284 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 1.8E-05 | cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 1.8E-05 | cm/cm/°C | |
| TD：-- | ISO 11359-2 | 5.5E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 5.5E-05 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| SpecificHeatCapacity of Melt | 1860 | J/kg/°C | ||
| Shrinkage rate | MD | ISO 294-4 | 0.20 | % |
| TD | ISO 294-4 | 0.60 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO 62 | 4.5 | % |
| ThermalConductivityofMelt | 0.25 | W/m/K | ||
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | IEC 60093 | -- | ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 36 | KV/mm | |
| Relative permittivity | 100Hz | IEC 60250 | 4.00 | |
| 1MHz | IEC 60250 | 4.00 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Sale | ISO 2039-2 | 124 | |
| M-Sale | ISO 2039-2 | 108 | ||
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| Odor | VDA270 | 4.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.